649813

PEDOT

tetramethacrylate end-capped solution, 0.5 wt. % (dispersion in propylene carbonate), contains p-toluenesulfonate as dopant

• Synonim(y): Oligotron^™ PC, PEDOT, PEDOT, tetramethacrylate end-capped
• Numer CAS: 126213-51-2
• Numer WE: 203-572-1
• Numer MDL: MFCD06798809
• Kod UNSPSC: 12352103
• NACRES: NA.23

Właściwości

• Nazwa produktu: Poly(3,4-ethylenedioxythiophene), tetramethacrylate end-capped solution, 0.5 wt. % (dispersion in propylene carbonate), contains p-toluenesulfonate as dopant
• masa cząsteczkowa: ~1,360-1,600 g/mol (methacrylate equivalent weight); average M_n ~6,000(lit.)
• Poziom jakości: 100
• zawiera: p-toluenesulfonate as dopant
• skład: Oligotron^™ tetramethacrylate, 0.5 wt. % ; propylene carbonate, 99.5 wt. %
• stężenie: 0.5 wt. % (dispersion in propylene carbonate)
• opór: 1-10 M Ω/sq (typical surface resistance of film)
• przewodność: 0.1-0.5 S/cm (bulk)
• gęstość: 1.189 g/mL at 25 °C

Opis

Opis ogólny

Główną cechą 4135 PC jest to, że zachowuje się jak reaktywny oligomer w nielotnym rozpuszczalniku. Stosowany w mieszaninach z monomerami lub w reakcjach ze związkami funkcjonalnymi.

Poli(3,4-etylenodioksytiofen), roztwór zakończony tetrametakrylanem (PEDOT-Meth) to polimer na bazie półprzewodników, który jest funkcjonalizowany tetrametakrylanem, który ułatwia skuteczne sieciowanie sprzężonych warstw.

Please follow this link for Aedotron/Oligotron selection guide table.

Zastosowanie

PEDOT-Meth może być stosowany jako membrana plastyfikująca w produkcji czujników jonoselektywnych i diod elektroluminescencyjnych.

For best results, agitate for 20 minutes prior to use. Films cast from propylene carbonate will require heat to dry. Photocurable inks can be formulated by adding acrylate monomers and photoinitiators (i.e. DMPA). Propylene carbonate will remain in the polymer. Functional compounds can be coupled to the oligomer via reactions at the methacrylate group.

Product can be blended with additional acrylate or methacrylate monomers and crosslinked to make polymer blends. Custom molecules can be synthesized by bonding functional compounds, via the methacrylate groups, to the conducting EDOT oligomers.

Cechy i korzyści

End-capped structure renders the conducting oligomer PEDOT dispersible. The methacrylate groups offer the potential for crosslinking, or addtional chemical functionalization. Completely dried Oligotron(TM) tetramethacrylate via the methacrylate functional groups.

Przestroga

Store this product at room temperature (do not refrigerate or freeze). Some settling will normally occur. Agitate, sonicate, and filter prior to use. A plug of glass wool in a pipette can be used for easy filtration. The shelf life of this product will vary depending on how it is stored and handled. Product should be discarded if heavy aggregation occurs, or if sonication / filtering are inadequate to produce a good casting solution.

Informacje prawne

Oligotron is a trademark of TDA Research, Inc.

Ta strona może zawierać tekst przetłumaczony maszynowo.

Informacja o środkach bezpieczeństwa

• Piktogramy: GHS07
• Hasło ostrzegawcze: Warning
• Zwroty wskazujące rodzaj zagrożenia: H319
• Zwroty wskazujące środki ostrożności: P305 + P351 + P338
• Klasyfikacja zagrożeń: Eye Irrit. 2
• Kod klasy składowania: 10 - Combustible liquids
• Klasa zagrożenia wodnego (WGK): WGK 2
• Temperatura zapłonu (°F): 269.6 °F - closed cup
• Temperatura zapłonu (°C): 132 °C - closed cup