181374
Polybutadiene, cis
average Mw 200,000-300,000
Zaloguj sięWyświetlanie cen organizacyjnych i kontraktowych
About This Item
Wzór liniowy:
(CH2CH=CHCH2)n
Numer CAS:
Numer MDL:
Kod UNSPSC:
12162002
Identyfikator substancji w PubChem:
NACRES:
NA.23
Polecane produkty
opis
98% cis
Formularz
slab/chunk
masa cząsteczkowa
average Mw 200,000-300,000
lepkość
40, Mooney(lit.)
temp. przejścia
Tg −102 °C
gęstość
0.9 g/mL at 25 °C (lit.)
ciąg SMILES
C\C=C\C
InChI
1S/C4H8/c1-3-4-2/h3-4H,1-2H3/b4-3+
Klucz InChI
IAQRGUVFOMOMEM-ONEGZZNKSA-N
Powiązane kategorie
Opis ogólny
Polybutadiene, cis (PB-cis) is a synthetic rubber that is prepared by solution polymerization of 1,4-butadiene. Its mechanical properties include low temperature flexibility and abrasion resistance. It can be cured by using sulfur based donors and peroxides and thus PB-cis acts as a highly cross-linked polymer with high resilience.
Zastosowanie
PB-cis can be polymerized with styrene for the formation of high impact polystyrene (HIPS). It may also be used as a toughening agent for acrylonitrile butadiene rubber (ABS) based resins.
Ta strona może zawierać tekst przetłumaczony maszynowo.
Kod klasy składowania
10 - Combustible liquids
Klasa zagrożenia wodnego (WGK)
WGK 3
Temperatura zapłonu (°F)
Not applicable
Temperatura zapłonu (°C)
Not applicable
Środki ochrony indywidualnej
Eyeshields, Gloves, type N95 (US)
Wybierz jedną z najnowszych wersji:
Masz już ten produkt?
Dokumenty związane z niedawno zakupionymi produktami zostały zamieszczone w Bibliotece dokumentów.
Rubber Basics, 80-81 (2002)
Morphological, mechanical properties, and fracture behavior of bulk-made ABS resins toughened by high-cis polybutadiene rubber
Yu Z, et al.
Polym. Eng. Sci., 50(5), 961-969 (2010)
Role of the rubber particle and polybutadiene cis content on the toughness of high impact polystyrene
Rovere J, et al.
Journal of materials science & technology, 43(3), 952-959 (2008)
Handbook of Poylmer-Liquid Interaction Parameters and Solubility Parameters (2018)
P S Brown et al.
Langmuir : the ACS journal of surfaces and colloids, 28(38), 13712-13719 (2012-09-13)
Two-dimensional hexagonally ordered honeycomb surfaces have been created by solvent casting polybutadiene films under controlled humidity. Subsequent CF(4) plasmachemical fluorination introduces cross-linking and surface texturing, leading to hierarchical surfaces with roughness on both the 10 μm (honeycomb) and micrometer (texturing)
Nasz zespół naukowców ma doświadczenie we wszystkich obszarach badań, w tym w naukach przyrodniczych, materiałoznawstwie, syntezie chemicznej, chromatografii, analityce i wielu innych dziedzinach.
Skontaktuj się z zespołem ds. pomocy technicznej