  • Charging of poly(methyl methacrylate) (PMMA) colloids in cyclohexyl bromide: locking, size dependence, and particle mixtures.

Charging of poly(methyl methacrylate) (PMMA) colloids in cyclohexyl bromide: locking, size dependence, and particle mixtures.

Langmuir : the ACS journal of surfaces and colloids (2014-12-24)
Marjolein N van der Linden, Johan C P Stiefelhagen, Gülşen Heessels-Gürboğa, Jessi E S van der Hoeven, Nina A Elbers, Marjolein Dijkstra, Alfons van Blaaderen
要旨

We studied suspensions of sterically stabilized poly(methyl methacrylate) (PMMA) particles in the solvent cyclohexyl bromide (CHB; εr = 7.92). We performed microelectrophoresis measurements on suspensions containing a single particle species and on binary mixtures, using confocal microscopy to measure the velocity profiles of the particles. We measured the charge of so-called locked PMMA particles, for which the steric stabilizer, a comb-graft stabilizer of poly(12-hydroxystearic acid) (PHSA) grafted on a backbone of PMMA, was covalently bonded to the particle, and for unlocked particles, for which the stabilizer was adsorbed to the surface of the particle. We observed that locked particles had a significantly higher charge than unlocked particles. We found that the charge increase upon locking was due to chemical coupling of 2-(dimethylamino)ethanol to the PMMA particles, which was used as a catalyst for the locking reaction. For particles of different size we obtained the surface potential and charge from the electrophoretic mobility of the particles. For locked particles we found that the relatively high surface potential (∼ +5.1 kBT/e or +130 mV) was roughly constant for all particle diameters we investigated (1.2 μm < σ < 4.4 μm), and that the particle charge was proportional to the square of the diameter.

材料
製品番号
ブランド
製品内容

Sigma-Aldrich
酸化アルミニウム, activated, basic, Brockmann I
Sigma-Aldrich
酸化アルミニウム, activated, neutral, Brockmann I
Sigma-Aldrich
酸化アルミニウム, powder, 99.99% trace metals basis
Sigma-Aldrich
酸化アルミニウム, activated, acidic, Brockmann I
Sigma-Aldrich
酸化アルミニウム, powder, primarily α phase, ≤10 μm avg. part. size, 99.5% trace metals basis
Sigma-Aldrich
酸化アルミニウム, nanopowder, <50 nm particle size (TEM)
Sigma-Aldrich
酸化アルミニウム, nanoparticles, <50 nm particle size (DLS), 20 wt. % in isopropanol
Sigma-Aldrich
酸化アルミニウム, Corundum, α-phase, -100 mesh
Sigma-Aldrich
酸化アルミニウム, pellets, 3 mm
Sigma-Aldrich
酸化アルミニウム, fused, powder, primarily α-phase, -325 mesh
Sigma-Aldrich
酸化アルミニウム, nanopowder, 13 nm primary particle size (TEM), 99.8% trace metals basis
Sigma-Aldrich
ブロモシクロヘキサン, 98%
Sigma-Aldrich
酸化アルミニウム, 99.997% trace metals basis
Sigma-Aldrich
酸化アルミニウム, Type WN-6, Neutral, Activity Grade Super I
Sigma-Aldrich
酸化アルミニウム, pore size 58 Å, ~150 mesh
Sigma-Aldrich
酸化アルミニウム, nanoparticles, 30-60 nm particle size (TEM), 20 wt. % in H2O
Sigma-Aldrich
酸化アルミニウム, fused, powder, primarily α-phase, 100-200 mesh
Sigma-Aldrich
酸化アルミニウム, single crystal substrate, <0001>
Sigma-Aldrich
酸化アルミニウム, nanowires, diam. × L 2-6 nm × 200-400 nm
Sigma-Aldrich
酸化アルミニウム、メソポーラス, MSU-X (wormhole), average pore size 3.8 nm
Sigma-Aldrich
酸化アルミニウム, activated, neutral, Brockmann I, free-flowing, Redi-Dri
Sigma-Aldrich
酸化アルミニウム, activated, acidic, Brockmann I, free-flowing, Redi-Dri
Supelco
酸化アルミニウム, activated, neutral, Brockmann Activity I
Sigma-Aldrich
酸化アルミニウム, CP
Sigma-Aldrich
酸化アルミニウム, SAJ special grade, ≥98.0%
Supelco
酸化アルミニウム, for the determination of hydrocarbons