Poly(oxy-1,4-phenyleneoxy-1,4-phenylenecarbonyl-1,4-phenylene)
Sinonimo/i:
PEEK, Polyether ether ketone
Autenticatiper visualizzare i prezzi riservati alla tua organizzazione & contrattuali
About This Item
Prodotti consigliati
Forma fisica
pellets
Durezza
126 (Rockwell R, ASTM D 785)
Punto di fusione
322 °C
Temp. transizione
Tm (DSC) 322 °C (onset)
Solubilità
all common solvents: insoluble
concentrated sulfuric acid: soluble
Densità
1.3 g/mL at 25 °C (lit.)
Stringa SMILE
Oc1ccc(O)cc1.Oc2ccc(cc2)C(=O)c3ccc(O)cc3
Cerchi prodotti simili? Visita Guida al confronto tra prodotti
Descrizione generale
Poly(oxy-1,4-phenyleneoxy-1,4-phenylenecarbonyl-1,4-phenylene)(PEEK) is a semi-crystalline polymer with good thermo-mechanical properties and high chemical resistance which can be used as engineering plastics.
Applicazioni
PEEK can be sulfonated and coated on nanofiltration(NF) membranes which can be used in the fabrication of antifouling based NF membranes. Sulfonated PEEK (up to 50-70 degree of sulfonation(DS)) can be used in the formation of proton exchange membranes(PEMs) for fuel cells based applications.
Codice della classe di stoccaggio
11 - Combustible Solids
Classe di pericolosità dell'acqua (WGK)
WGK 3
Punto d’infiammabilità (°F)
Not applicable
Punto d’infiammabilità (°C)
Not applicable
Dispositivi di protezione individuale
Eyeshields, Gloves, type N95 (US)
Scegli una delle versioni più recenti:
Possiedi già questo prodotto?
I documenti relativi ai prodotti acquistati recentemente sono disponibili nell’Archivio dei documenti.
I clienti hanno visto anche
Effects of sulfonated polyether-etherketone (SPEEK) and composite membranes on the proton exchange membrane fuel cell (PEMFC) performance.
International Journal of Hydrogen Energy, 34(10), 4645-4652 (2009)
Preparation and characterization of a neutrally charged antifouling nanofiltration membrane by coating a layer of sulfonated poly (ether ether ketone) on a positively charged nanofiltration membrane.
Journal of Membrane Science, 362(1-2), 192-201 (2010)
Proton conducting composite membranes from polyether ether ketone and heteropolyacids for fuel cell applications.
Journal of Membrane Science , 173(1), 17-34 (2000)
Glass transition and melting behavior of poly (oxy-1, 4-phenyleneoxy-1, 4-phenylenecarbonyl-1, 4-phenylene)(PEEK).
Macromolecules, 19(7), 1868-1876 (1986)
Sulfonated poly (ether ether ketone) membranes for direct methanol fuel cell.
Journal of Membrane Science , 226(1-2), 159-167 (2003)
Il team dei nostri ricercatori vanta grande esperienza in tutte le aree della ricerca quali Life Science, scienza dei materiali, sintesi chimica, cromatografia, discipline analitiche, ecc..
Contatta l'Assistenza Tecnica.