Titanium dioxide nanotube modified implants: an animal study on bone formation.

Titanium dioxide nanotube modified implants: an animal study on bone formation.

Journal of nanoscience and nanotechnology (2013-07-19)

Kwi-Dug Yun, Sang-Won Park, Kwang-Min Lee, Hyun-Seung Kim, Mong-Sook Vang, Hong-So Yang, Jeong-Tae Koh, Seong-Soo Kang, Gye-Jeong Oh, Ga-Hyun Kim, Min-Kyung Ji, Gab-Woon Hwang, Hyun-Pil Lim

要旨

This study examined the bone response to titanium dioxide nanotube modified implants. A total of 24 implants were placed in the femur of 4 beagles. Before placement, screw-shaped implants were classified into 3 groups; machined surface (group M), titanium dioxide nanotube modification of the machined surface (group MN) and titanium dioxide nanotube modification of the RBM surface (group RN). The texture morphology was observed via scanning electron microscopy. Animals were euthanized after 4 and 12 weeks of submerged healing and the histologic and histomorphometric analyses were performed. Groups MN and RN showed a significantly higher percentage of mineralized bone than that in group M (p < 0.05). The results of this in vivo study constitute significant evidence that the presence of the titanium dioxide nanotubes enhance osseointegration of implants.

材料

製品番号

ブランド

製品内容

Sigma-Aldrich

酸化チタン(IV), nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

Sigma-Aldrich

酸化チタン(IV)、アナターゼ, nanopowder, <25 nm particle size, 99.7% trace metals basis

Sigma-Aldrich

酸化チタン(IV), puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%

Sigma-Aldrich

酸化チタン(IV)、アナターゼ, powder, 99.8% trace metals basis

Sigma-Aldrich

酸化チタン(IV), ReagentPlus^®, ≥99%

Sigma-Aldrich

酸化チタン(IV)、ルチル, powder, <5 μm, ≥99.9% trace metals basis

Sigma-Aldrich

酸化チタン(IV)、ルチル型/アナターゼ型混合物, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

Sigma-Aldrich

酸化チタン(IV)、アナターゼ, powder, −325 mesh, ≥99% trace metals basis

Sigma-Aldrich

酸化チタン(IV)、ルチル, nanopowder, <100 nm particle size, 99.5% trace metals basis

Sigma-Aldrich

酸化チタン(IV)、ルチル型/アナターゼ型混合物, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 0.127 mm, 99.7% trace metals basis

Sigma-Aldrich

チタン, powder, <45 μm avg. part. size, 99.98% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 0.25 mm, 99.7% trace metals basis

Sigma-Aldrich

酸化チタン(IV)、ルチル, 99.995% trace metals basis

Sigma-Aldrich

チタン, powder, −100 mesh, 99.7% trace metals basis

Sigma-Aldrich

酸化チタン(IV)、ルチル, ≥99.98% trace metals basis

Sigma-Aldrich

酸化チタン(IV), contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

Sigma-Aldrich

チタン, foil, thickness 2.0 mm, 99.7% trace metals basis

Sigma-Aldrich

チタン, wire, diam. 1.0 mm, 99.99% trace metals basis

Sigma-Aldrich

チタン, wire, diam. 0.25 mm, 99.7% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 0.127 mm, ≥99.99% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 0.025 mm, 99.98% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 0.5 mm, 99.99% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 0.25 mm, 99.99% trace metals basis