Hydroxyapatite coatings on nanotubular titanium dioxide thin films prepared by radio frequency magnetron sputtering.

Hydroxyapatite coatings on nanotubular titanium dioxide thin films prepared by radio frequency magnetron sputtering.

Journal of nanoscience and nanotechnology (2013-07-26)

Jinho Shin, Kwangmin Lee, Jeongtae Koh, Hyeju Son, Hyunseung Kim, Hyun-Pil Lim, Kwidug Yun, Gyejeong Oh, Seokwoo Lee, Heekyun Oh, Kyungku Lee, Gabwoon Hwang, Sang-Won Park

要旨

In this study, hydroxyapatite (HA) was coated on anodized titanium (Ti) surfaces through radio frequency magnetron sputtering in order to improve biological response of the titanium surface. All the samples were blasted with resorbable blasting media (RBM). RBM-blasted Ti surface, anodized Ti surface, as-sputtered HA coating on the anodized Ti surface, and heat-treated HA coating on the anodized Ti surface were prepared. The samples were characterized using scanning electron microscopy and X-ray photoemission spectroscopy, and biologic responses were evaluated. The top of the TiO2 nanotubes was not closed by HA particles when the coating time is less than 15 minutes. It was demonstrated that the heat-treated HA was well-crystallized and this enhanced the cell attachment of the anodized Ti surface.

材料

製品番号

ブランド

製品内容

Sigma-Aldrich

チタン, powder, <45 μm avg. part. size, 99.98% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 0.127 mm, 99.7% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 0.25 mm, 99.7% trace metals basis

Sigma-Aldrich

チタン, powder, −100 mesh, 99.7% trace metals basis

Sigma-Aldrich

チタン, wire, diam. 0.25 mm, 99.7% trace metals basis

Sigma-Aldrich

チタン, sponge, 3-19 mm, 99.5% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 2.0 mm, 99.7% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 0.025 mm, 99.98% trace metals basis

Sigma-Aldrich

ヒドロキシアパタイト, puriss., meets analytical specification of Ph. Eur., BP, FCC, E341, ≥90% (calculated on glowed substance)

Sigma-Aldrich

チタン, foil, thickness 0.5 mm, 99.99% trace metals basis

Sigma-Aldrich

チタン, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis

Sigma-Aldrich

チタン, wire, diam. 1.0 mm, 99.99% trace metals basis

Sigma-Aldrich

チタン, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

Sigma-Aldrich

ヒドロキシアパタイト, purum p.a., ≥90% (as Ca₃(PO₄)₂, KT)

Sigma-Aldrich

チタン, foil, thickness 0.127 mm, ≥99.99% trace metals basis

Sigma-Aldrich

チタン, foil, thickness 0.25 mm, 99.99% trace metals basis

Sigma-Aldrich

ヒドロキシアパタイト, SAJ first grade, 98.0-103.0%

Sigma-Aldrich

チタン, wire, diam. 0.81 mm, 99.7% trace metals basis

Sigma-Aldrich

チタン, wire, diam. 0.5 mm, 99.99% trace metals basis

Sigma-Aldrich

ヒドロキシアパタイト, Type I, buffered aqueous suspension

Sigma-Aldrich

チタン, evaporation slug, diam. × L 6.3 mm × 6.3 mm, ≥99.99% trace metals basis

チタン, IRMM^®, certified reference material, 0.1 mm foil

チタン, IRMM^®, certified reference material, 0.5 mm foil

チタン, IRMM^®, certified reference material, 0.5 mm wire