181153
Nylon 11
pellets, 3 mm
Sinonimo/i:
Polyundecanolactam
Autenticatiper visualizzare i prezzi riservati alla tua organizzazione & contrattuali
About This Item
Formula condensata:
[-NH(CH2)10CO-]n
Numero CAS:
Peso molecolare:
201.31
Numero MDL:
Codice UNSPSC:
12162002
ID PubChem:
NACRES:
NA.23
Prodotti consigliati
Stato
pellets
Livello qualitativo
Dimensione particelle
3 mm
Temp. transizione
Tm 198 °C
Tg 46 °C
Densità
1.026 g/mL at 25 °C (lit.)
Stringa SMILE
NCCCCCCCCCCC(O)=O
InChI
1S/C33H65N3O3/c34-28-22-16-10-4-2-8-14-20-26-32(38)36-30-24-18-12-6-3-9-15-21-27-33(39)35-29-23-17-11-5-1-7-13-19-25-31-37/h31H,1-30,34H2,(H,35,39)(H,36,38)
IAPYCAVXWCDYGR-UHFFFAOYSA-N
Categorie correlate
Codice della classe di stoccaggio
11 - Combustible Solids
Classe di pericolosità dell'acqua (WGK)
WGK 3
Punto d’infiammabilità (°F)
Not applicable
Punto d’infiammabilità (°C)
Not applicable
Scegli una delle versioni più recenti:
Possiedi già questo prodotto?
I documenti relativi ai prodotti acquistati recentemente sono disponibili nell’Archivio dei documenti.
I clienti hanno visto anche
Valeria Bugatti et al.
Nanomaterials (Basel, Switzerland), 8(3) (2018-03-02)
Bio-based membranes were obtained using Polyamide 11 (PA11) from renewable sources and a nano-hybrid composed of halloysite nanotubes (HNTs) filled with lysozyme (50 wt % of lysozyme), as a natural antimicrobial molecule. Composites were prepared using an electrospinning process, varying
Valeria Bugatti et al.
Polymers, 11(4) (2019-04-10)
Antimicrobial packaging systems are recognized as effective approaches to prolong food shelf life. In this context, Bio-based PA11 loaded with a food-grade zeolite were prepared using ball milling technology in the dry state. Zeolite was filled with sodium salicylate, as
María Elena Sánchez-Vergara et al.
Polymers, 12(1) (2019-12-22)
Chemical degradation is a major disadvantage in the development of organic semiconductors. This work proposes the manufacture and characterization of organic semiconductor membranes in order to prevent semiconductor properties decreasing. Semiconductor membranes consisting of Nylon-11 and particles of π-conjugated molecular
Il team dei nostri ricercatori vanta grande esperienza in tutte le aree della ricerca quali Life Science, scienza dei materiali, sintesi chimica, cromatografia, discipline analitiche, ecc..
Contatta l'Assistenza Tecnica.