Self-cleaning and mechanical properties of modified white cement with nanostructured TiO2.

Self-cleaning and mechanical properties of modified white cement with nanostructured TiO2.

Journal of nanoscience and nanotechnology (2013-08-02)

R Khataee, V Heydari, L Moradkhannejhad, M Safarpour, S W Joo

摘要

In the present study, self-cleaning and mechanical properties of white Portland cement by addition of commercial available TiO2 nanoparticles with the average particle size of 80 nm were investigated. X-ray diffraction (XRD), transmission electron microscopy (TEM) and BET were used to characterize TiO2 nanoparticles. For determination of self-cleaning properties of TiO2-modified white cement, colorimetric tests in decolorization of C.I. Basic Red 46 (BR46) in comparison to unmodified cement samples was applied. The results indicated that with increasing the amount of TiO2 nanoparticles in modified cement, self-cleaning property of the samples increased. The mechanical properties of TiO2-modified and unmodified cement samples, such as time of setting of hydraulic cement, compressive strength of hydraulic cement mortar and flexural strength of hydraulic cement mortar were examined. The results indicated that addition of TiO2 nanoparticles up to maximum replacement level of 1.0% improved compressive and flexural strength and decreased its setting time.

材料

货号

品牌

产品描述

718467

Sigma-Aldrich

氧化钛（IV）, nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

637254

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, nanopowder, <25 nm particle size, 99.7% trace metals basis

14027

Sigma-Aldrich

氧化钛（IV）, puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%

232033

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, powder, 99.8% trace metals basis

14021

Sigma-Aldrich

氧化钛（IV）, ReagentPlus^®, ≥99%

224227

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, powder, <5 μm, ≥99.9% trace metals basis

248576

Sigma-Aldrich

氧化钛 (IV)，锐钛矿, powder, −325 mesh, ≥99% trace metals basis

637262

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, nanopowder, <100 nm particle size, 99.5% trace metals basis

634662

Sigma-Aldrich

氧化钛(IV)，金红石和锐钛矿混合物, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

348791

Sigma-Aldrich

钛, foil, thickness 0.127 mm, 99.7% trace metals basis

366994

Sigma-Aldrich

钛, powder, <45 μm avg. part. size, 99.98% trace metals basis

267503

Sigma-Aldrich

钛, foil, thickness 0.25 mm, 99.7% trace metals basis

700347

Sigma-Aldrich

氧化钛(IV)，金红石和锐钛矿混合物, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

268496

Sigma-Aldrich

钛, powder, −100 mesh, 99.7% trace metals basis

204757

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, ≥99.98% trace metals basis

204730

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, 99.995% trace metals basis

677469

Sigma-Aldrich

氧化钛（IV）, contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

460400

Sigma-Aldrich

钛, wire, diam. 0.25 mm, 99.7% trace metals basis

268526

Sigma-Aldrich

钛, sponge, 1-20 mm, 99.5% trace metals basis

369489

Sigma-Aldrich

钛, foil, thickness 2.0 mm, 99.7% trace metals basis

348848

Sigma-Aldrich

钛, foil, thickness 0.025 mm, 99.98% trace metals basis

348805

Sigma-Aldrich

钛, foil, thickness 0.5 mm, 99.99% trace metals basis

767506

Sigma-Aldrich

钛, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis

460397

Sigma-Aldrich

钛, foil, thickness 0.127 mm, ≥99.99% trace metals basis

266035

Sigma-Aldrich

钛, wire, diam. 1.0 mm, 99.99% trace metals basis

635057

Sigma-Aldrich

钛 (IV) 氧化物，金红石型, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

267481

Sigma-Aldrich

钛, foil, thickness 0.25 mm, 99.99% trace metals basis

305812

Sigma-Aldrich

钛, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

348864

Sigma-Aldrich

钛, wire, diam. 0.5 mm, 99.99% trace metals basis

267902

Sigma-Aldrich

钛, wire, diam. 0.81 mm, 99.7% trace metals basis