Hydroxyapatite

powder, 10 μm

Sinonimo/i:

Apatite hydroxide, Hydroxylapatite

Autenticatiper visualizzare i prezzi riservati alla tua organizzazione & contrattuali
Tutte le immagini(2)

About This Item

Formula condensata:
Ca10(PO4)6(OH)2
Numero CAS:
1306-06-5
Numero CE:
215-145-7
Codice UNSPSC:
12352305

Livello qualitativo

100

Descrizione

Total Heavy Metals: ≤20 ppm

Forma fisica

powder

Area superficiale

≥80 m2/g

Dimensione particelle

10 μm±2.0 μm

InChI

1S/5Ca.3H3O4P.H2O/c;;;;;3*1-5(2,3)4;/h;;;;;3*(H3,1,2,3,4);1H2/q5*+2;;;;/p-10
XYJRXVWERLGGKC-UHFFFAOYSA-D

Cerchi prodotti simili? Visita Guida al confronto tra prodotti

Categorie correlate

Applicazioni

Hydroxyapatite and tricalcium phosphate are bioactive ceramic materials and they find applications as bone grafts, fillers and coating material for metal implants.

Codice della classe di stoccaggio

13 - Non Combustible Solids

Classe di pericolosità dell'acqua (WGK)

WGK 1

Punto d’infiammabilità (°F)

Not applicable

Punto d’infiammabilità (°C)

Not applicable

Certificati d'analisi (COA)

Cerca il Certificati d'analisi (COA) digitando il numero di lotto/batch corrispondente. I numeri di lotto o di batch sono stampati sull'etichetta dei prodotti dopo la parola ‘Lotto’ o ‘Batch’.

Possiedi già questo prodotto?

I documenti relativi ai prodotti acquistati recentemente sono disponibili nell’Archivio dei documenti.

Visita l’Archivio dei documenti

I clienti hanno visto anche

Slide 1 of 4

1 of 4

Sigma-Aldrich

Sigma-Aldrich

902403

3D Printing Hydroxyapatite ink

Tricalcium phosphate powder, 4 μm, ≥80 m2g

Sigma-Aldrich

900205

Tricalcium phosphate

Tribasic calcium phosphate United States Pharmacopeia (USP) Reference Standard

USP

1087031

Tribasic calcium phosphate

Hydroxylapatite, Fast Flow

Sigma-Aldrich

391947

Hydroxylapatite, Fast Flow

Liu Y, et al.
Carbon, 76, 250-250 (2014)
Lu Xie et al.
Materials science & engineering. C, Materials for biological applications, 59, 1007-1015 (2015-12-15)
The ideal bone tissue engineering scaffolds are long-cherished with the properties of interconnected macroporous structures, adjustable degradation and excellent biocompatibility. Here, a series of porous α/β-tricalcium phosphate (α/β-TCP) biphasic bioceramics with different phase ratios of α-TCP and β-TCP were successfully
Sahar Vahabzadeh et al.
Acta biomaterialia, 17, 47-55 (2015-02-02)
In this work we have investigated the effects of strontium (Sr) dopant on in vitro protein release kinetics and in vivo osteogenic properties of plasma sprayed hydroxyapatite (HA) coatings, along with their dissolution behavior. Plasma sprayed HA coatings are widely
Sophie C Cox et al.
Materials science & engineering. C, Materials for biological applications, 47, 237-247 (2014-12-11)
A systematic characterisation of bone tissue scaffolds fabricated via 3D printing from hydroxyapatite (HA) and poly(vinyl)alcohol (PVOH) composite powders is presented. Flowability of HA:PVOH precursor materials was observed to affect mechanical stability, microstructure and porosity of 3D printed scaffolds. Anisotropic

Il team dei nostri ricercatori vanta grande esperienza in tutte le aree della ricerca quali Life Science, scienza dei materiali, sintesi chimica, cromatografia, discipline analitiche, ecc..

Contatta l'Assistenza Tecnica.