267554
Tungsten
wire, diam. 0.25 mm, ≥99.9% trace metals basis
Sinonimo/i:
W
Autenticatiper visualizzare i prezzi riservati alla tua organizzazione & contrattuali
About This Item
Formula empirica (notazione di Hill):
W
Numero CAS:
Peso molecolare:
183.84
Numero CE:
Numero MDL:
Codice UNSPSC:
12141747
ID PubChem:
NACRES:
NA.23
Prodotti consigliati
Livello qualitativo
Saggio
≥99.9% trace metals basis
Forma fisica
wire
Resistività
4.9 μΩ-cm, 20°C
Diametro
0.25 mm
P. eboll.
5660 °C (lit.)
Punto di fusione
3410 °C (lit.)
Densità
19.3 g/mL at 25 °C (lit.)
Stringa SMILE
[W]
InChI
1S/W
WFKWXMTUELFFGS-UHFFFAOYSA-N
Applicazioni
Tungsten (W) wire can be used for a variety of applications such as:
- fabrication of tungsten tips which can be used as field emitters, nanoprobes and scanning tunneling microscope (STM) probes.
- increase of the band gap of amorphous silicon germanium alloy.
- formation of tungsten fibers for potential usage in the lighting industry.
Quantità
9.5 g = 10 m; 95 g = 100 m
Codice della classe di stoccaggio
11 - Combustible Solids
Classe di pericolosità dell'acqua (WGK)
nwg
Punto d’infiammabilità (°F)
Not applicable
Punto d’infiammabilità (°C)
Not applicable
Dispositivi di protezione individuale
dust mask type N95 (US), Eyeshields, Gloves, type P3 (EN 143) respirator cartridges
Scegli una delle versioni più recenti:
Possiedi già questo prodotto?
I documenti relativi ai prodotti acquistati recentemente sono disponibili nell’Archivio dei documenti.
I clienti hanno visto anche
Recrystallization of tungsten wire for fabrication of sharp and stable nanoprobe and field-emitter tips
Greiner M and Kruse P
The Review of Scientific Instruments, 78(2), 026104-026104 (2007)
Improving narrow bandgap a-SiGe: H alloys grown by hot-wire chemical vapor deposition
Xu Y, et al.
Thin Solid Films, 430(1-2), 197-201 (2003)
Tungsten fibre-reinforced composites for advanced plasma facing components
Neu R, et al.
Nuclear Materials and Energy, 12(1-2), 1308-1313 (2017)
Weijie Zhao et al.
ACS nano, 7(1), 791-797 (2012-12-22)
Geometrical confinement effect in exfoliated sheets of layered materials leads to significant evolution of energy dispersion in mono- to few-layer thickness regime. Molybdenum disulfide (MoS(2)) was recently found to exhibit indirect-to-direct gap transition when the thickness is reduced to a
Zhigang Chen et al.
Advanced materials (Deerfield Beach, Fla.), 25(14), 2095-2100 (2013-02-22)
A new photothermal coupling agent for photothermal ablation (PTA) therapy of tumors is developed based on ultrathin PEGylated W18O49 nanowires. After being injected with the nanowire solution, the in vivo tumors exhibit a rapid temperature rise to 50.0 ± 0.5
Il team dei nostri ricercatori vanta grande esperienza in tutte le aree della ricerca quali Life Science, scienza dei materiali, sintesi chimica, cromatografia, discipline analitiche, ecc..
Contatta l'Assistenza Tecnica.