Self-cleaning and mechanical properties of modified white cement with nanostructured TiO2.

Self-cleaning and mechanical properties of modified white cement with nanostructured TiO2.

Journal of nanoscience and nanotechnology (2013-08-02)

R Khataee, V Heydari, L Moradkhannejhad, M Safarpour, S W Joo

ABSTRACT

In the present study, self-cleaning and mechanical properties of white Portland cement by addition of commercial available TiO2 nanoparticles with the average particle size of 80 nm were investigated. X-ray diffraction (XRD), transmission electron microscopy (TEM) and BET were used to characterize TiO2 nanoparticles. For determination of self-cleaning properties of TiO2-modified white cement, colorimetric tests in decolorization of C.I. Basic Red 46 (BR46) in comparison to unmodified cement samples was applied. The results indicated that with increasing the amount of TiO2 nanoparticles in modified cement, self-cleaning property of the samples increased. The mechanical properties of TiO2-modified and unmodified cement samples, such as time of setting of hydraulic cement, compressive strength of hydraulic cement mortar and flexural strength of hydraulic cement mortar were examined. The results indicated that addition of TiO2 nanoparticles up to maximum replacement level of 1.0% improved compressive and flexural strength and decreased its setting time.

MATERIALS

Product Number

Brand

Product Description

700347

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanoparticles, <150 nm particle size (volume distribution, DLS), dispersion, 40 wt. % in H₂O, 99.5% trace metals basis

634662

Sigma-Aldrich

Titanium(IV) oxide, mixture of rutile and anatase, nanopowder, <100 nm particle size (BET), 99.5% trace metals basis

637262

Sigma-Aldrich

Titanium(IV) oxide, rutile, nanopowder, <100 nm particle size, 99.5% trace metals basis

635057

Sigma-Aldrich

Titanium(IV) oxide, rutile, <001>, (single crystal substrate), ≥99.9% trace metals basis, L × W × thickness 10 mm × 10 mm × 0.5 mm

718467

Sigma-Aldrich

Titanium(IV) oxide, nanopowder, 21 nm primary particle size (TEM), ≥99.5% trace metals basis

14021

Sigma-Aldrich

Titanium(IV) oxide, ReagentPlus^®, ≥99%

14027

Sigma-Aldrich

Titanium(IV) oxide, puriss., meets analytical specification of Ph. Eur., BP, USP, 99-100.5%

IRMM531B

Titanium, IRMM^®, certified reference material, 0.5 mm foil

IRMM531C

Titanium, IRMM^®, certified reference material, 0.5 mm wire

266035

Sigma-Aldrich

Titanium, wire, diam. 1.0 mm, 99.99% trace metals basis

305812

Sigma-Aldrich

Titanium, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

267902

Sigma-Aldrich

Titanium, wire, diam. 0.81 mm, 99.7% trace metals basis

460400

Sigma-Aldrich

Titanium, wire, diam. 0.25 mm, 99.7% trace metals basis

369489

Sigma-Aldrich

Titanium, foil, thickness 2.0 mm, 99.7% trace metals basis

677469

Sigma-Aldrich

Titanium(IV) oxide, contains 1% Mn as dopant, nanopowder, <100 nm particle size (BET), ≥97%

204730

Sigma-Aldrich

Titanium(IV) oxide, rutile, 99.995% trace metals basis

224227

Sigma-Aldrich

Titanium(IV) oxide, rutile, powder, <5 μm, ≥99.9% trace metals basis

204757

Sigma-Aldrich

Titanium(IV) oxide, rutile, ≥99.98% trace metals basis

348791

Sigma-Aldrich

Titanium, foil, thickness 0.127 mm, 99.7% trace metals basis

348848

Sigma-Aldrich

Titanium, foil, thickness 0.025 mm, 99.98% trace metals basis

IRMM531A

Titanium, IRMM^®, certified reference material, 0.1 mm foil

433667

Sigma-Aldrich

Titanium, evaporation slug, diam. × L 6.3 mm × 6.3 mm, ≥99.99% trace metals basis

637254

Sigma-Aldrich

Titanium(IV) oxide, anatase, nanopowder, <25 nm particle size, 99.7% trace metals basis

767506

Sigma-Aldrich

Titanium, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis