Electro-catalytic activity of palladium modified nitrogen doped titania nanoparticles.

Electro-catalytic activity of palladium modified nitrogen doped titania nanoparticles.

Journal of nanoscience and nanotechnology (2014-04-17)

Bijuan Zheng, Bei Qi, Yulong Hu, Fan Zhang, Hongfang Liu

摘要

Pd-modified N-doped TiO2 nanoparticles were prepared by the sol-gel method. The X-ray diffraction (XRD) pattern indicated that the pure anatase TiO2 has been obtained. Transmission electron microscope (TEM) was used to observe the micro-morphology of the nanoparticles. The average size of the particles was 8.04 nm. The N2 adsorption isotherm of the resulted nanoparticles was the type IV with a H1 type hysteresis loop. The specific surface area was 145.2 m2 g(-1) and the average diameter of adsorption was 4.178 nm. These Pd-modified N-doped TiO2 nanoparticles were applied onto the surface of glass carbon electrode (GCE), and its electro-catalytic activity was tested by cyclic voltammetry (CV). The reduction peak currents showed a linear response to the dissolved oxygen (DO) concentrations ranging from 0.6 mg L(-1) to 7.2 mg L(-1) on the Pd-N-TiO2/ GCE. The linear regression equation was y = 3E - 6x + 1E-5 (R = 0.9909). The detection limit was 0.22 mg L(-1.) The result indicated that the Pd-N-TiO2 possessed a good electro-catalytic activity.

材料

货号

品牌

产品描述

348791

Sigma-Aldrich

钛, foil, thickness 0.127 mm, 99.7% trace metals basis

366994

Sigma-Aldrich

钛, powder, <45 μm avg. part. size, 99.98% trace metals basis

267503

Sigma-Aldrich

钛, foil, thickness 0.25 mm, 99.7% trace metals basis

268496

Sigma-Aldrich

钛, powder, −100 mesh, 99.7% trace metals basis

460400

Sigma-Aldrich

钛, wire, diam. 0.25 mm, 99.7% trace metals basis

268526

Sigma-Aldrich

钛, sponge, 1-20 mm, 99.5% trace metals basis

369489

Sigma-Aldrich

钛, foil, thickness 2.0 mm, 99.7% trace metals basis

GF16031843

钛, mesh, 100x100mm, nominal aperture 0.19mm, wire diameter 0.23mm, 60x60 wires/inch, open area 20%, twill weave

348848

Sigma-Aldrich

钛, foil, thickness 0.025 mm, 99.98% trace metals basis

348805

Sigma-Aldrich

钛, foil, thickness 0.5 mm, 99.99% trace metals basis

767506

Sigma-Aldrich

钛, sputtering target, diam. × thickness 2.00 in. × 0.25 in., 99.995% trace metals basis

GF29374005

钛, mesh, 100x100mm, nominal aperture 4.3mm, wire diameter 1.5mm, 4.4x4.4 wires/inch, open area 94%, platinized diamond mesh

460397

Sigma-Aldrich

钛, foil, thickness 0.127 mm, ≥99.99% trace metals basis

266035

Sigma-Aldrich

钛, wire, diam. 1.0 mm, 99.99% trace metals basis

267481

Sigma-Aldrich

钛, foil, thickness 0.25 mm, 99.99% trace metals basis

305812

Sigma-Aldrich

钛, 5-10 mm, ≥99.99% trace metals basis (purity exclusive of Na and K content)

348864

Sigma-Aldrich

钛, wire, diam. 0.5 mm, 99.99% trace metals basis

267902

Sigma-Aldrich

钛, wire, diam. 0.81 mm, 99.7% trace metals basis

GF31127712

钛, rod, 10mm, diameter 50mm, 99.99+%

GF14990935

钛, tube, 1000mm, outside diameter 10.3mm, inside diameter 8.7mm, wall thickness 0.8mm, annealed, 99.6+%

GF46592949

钛, wire, straight, 1000mm, diameter 1.0mm, as drawn, 99.6+%

433667

Sigma-Aldrich

钛, evaporation slug, diam. × L 6.3 mm × 6.3 mm, ≥99.99% trace metals basis

GF62977540

钛, tube, 200mm, outside diameter 2.03mm, inside diameter 1.63mm, wall thickness 0.2mm, annealed, 99.6+%

GF86399106

钛, tube, 500mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%

GF13900205

钛, tube, 100mm, outside diameter 0.51mm, inside diameter 0.35mm, wall thickness 0.08mm, annealed, 99.6+%

GF49264713

钛, tube, 200mm, outside diameter 1.6mm, inside diameter 1.2mm, wall thickness 0.2mm, hard, 99.6+%

GF95731960

钛, tube, 500mm, outside diameter 3.0mm, inside diameter 1.5mm, wall thickness 0.75mm, annealed, 99.6+%

GF04311638

钛, rod, 100mm, diameter 6mm, annealed, 99.6+%

GF96834493

钛, rod, 1000mm, diameter 5mm, annealed, 99.6+%

GF43519945

钛, wire reel, 2m, diameter 1.0mm, as drawn, 99.99+%