Preparation of cocrystal nanofibres of cobalt octaethylporphyrin and tetracyanoquinodimethane with good photoresponse.

Preparation of cocrystal nanofibres of cobalt octaethylporphyrin and tetracyanoquinodimethane with good photoresponse.

Journal of nanoscience and nanotechnology (2014-04-18)

Hao-Di Wu, Yan Xiao, Feng-Xia Wang, Ge-Bo Pan

ABSTRACT

Cocrystal nanofibres of cobalt octaethylporphyrin and tetracyanoquinodimethane were prepared by a facile solution method and fully characterized by SEM, AFM, XRD, Raman, EDX, and UV-vis-NIR. The as-prepared cocrystal nanofibres had smooth surfaces and uniform dimension. When incorporated into prototype devices, they exhibited good photoresponse at ambient conditions. Additionally, the phototransistor characteristics with a maximum I(on)/I(off) ratio of -460 was demonstrated. The facile synthesis and good photoresponse may boost the potential applications of cocrystal-based nanostructures in future miniaturized devices.

MATERIALS

Product Number

Brand

Product Description

Sigma-Aldrich

Cobalt, foil, thickness 1.0 mm, 99.95% trace metals basis

Sigma-Aldrich

Cobalt, powder, 2 μm particle size, 99.8% trace metals basis

Sigma-Aldrich

Cobalt, rod, diam. 5.0 mm, 99.95% trace metals basis

Sigma-Aldrich

Cobalt, foil, thickness 0.1 mm, 99.95% trace metals basis

Sigma-Aldrich

Cobalt, powder, <150 μm, ≥99.9% trace metals basis

Sigma-Aldrich

Cobalt, granular, 99.99% trace metals basis

Sigma-Aldrich

Cobalt, pieces, 99.5% trace metals basis

Sigma-Aldrich

Cobalt, wire, diam. 1.0 mm, 99.995% trace metals basis

Cobalt, foil, 4mm disks, thickness 0.008mm, 99.9%

Cobalt, foil, 8mm disks, thickness 0.015mm, 99.9%

Cobalt, foil, 6mm disks, thickness 0.0125mm, 99.9%

Cobalt, foil, 6mm disks, thickness 0.01mm, 99.9%

Cobalt, foil, not light tested, 50x50mm, thickness 0.006mm, 99.9%

Cobalt, foil, 8mm disks, thickness 0.25mm, as rolled, 99.9%

Cobalt, foil, 6mm disks, thickness 0.25mm, as rolled, 99.99+%

Cobalt, foil, light tested, 50x50mm, thickness 0.015mm, 99.9%

Cobalt, microfoil, disks, 10mm, thinness 0.5μm, specific density 434μg/cm², permanent mylar 3.5μm support, 99.9%

Cobalt, foil, not light tested, 25x25mm, thickness 0.006mm, 99.9%

Cobalt, foil, 8mm disks, thickness 0.01mm, 99.9%

Cobalt, foil, not light tested, 100x100mm, thickness 0.0125mm, 99.9%

Cobalt, foil, 6mm disks, thickness 0.025mm, 99.9%

Cobalt, foil, light tested, 25x25mm, thickness 0.009mm, 99.9%

Cobalt, wire reel, 0.05m, diameter 2.0mm, hard, 99.99+%

Cobalt, foil, not light tested, 50x50mm, thickness 0.007mm, 99.9%

Cobalt, foil, 8mm disks, thickness 0.25mm, as rolled, 99.99+%

Cobalt, foil, 8mm disks, thickness 0.003mm, 99.9%

Cobalt, foil, not light tested, 25x25mm, thickness 0.002mm, temporary acrylic support, 99.9%

Cobalt, foil, light tested, 50x50mm, thickness 0.01mm, 99.9%

Cobalt, foil, not light tested, 50x50mm, thickness 0.0025mm, temporary acrylic support, 99.9%

Cobalt, foil, 8mm disks, thickness 0.025mm, 99.9%