768642
Poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate)
1.0 wt. % in H2O, high-conductivity grade
Synonym(s):
Orgacon™ HIL-1005, PEDOT:PSS, Poly(2,3-dihydrothieno-1,4-dioxin)-poly(styrenesulfonate)
Sign Into View Organizational & Contract Pricing
All Photos(1)
About This Item
MDL number:
UNSPSC Code:
12352103
grade
high-conductivity grade
form
liquid
concentration
1.0 wt. % in H2O
resistance
50-120 Ω/sq
refractive index
n20/D 1.341
pH
1.8-2.2
viscosity
7-12 mPa.s(22 °C) (typical)
density
1.002 g/mL at 25 °C
Looking for similar products? Visit Product Comparison Guide
General description
A conducting polymer such as poly(3,4-ethylenedioxythiophene) doped with poly(styrene sulfonate) anions (PEDOT/PSS) is widely used in various organic optoelectronic devices. PEDOT: PSS is a blend of cationic polythiopene derivative, doped with a polyanion. High electrical conductivity and good oxidation resistance of such polymers make it suitable for electromagnetic shielding and noise suppression. Thus, the polymer film was found to possess high transparency throughout the visible light spectrum and even into near IR and near UV regions, virtually 100% absorption from 900-2,000 nm. No absorption maximum from 400-800 nm. Impact of small electric and magnetic fields on the polymer was studied.
Poly(3,4-ethylenedioxythiophene)-poly(styrenesulfonate) (PEDOT:PSS) is a conductive polymer that is formed by electropolymerizing 3,4-ethylenedioxythiophene in a solution of poly(styrenesulfonate)(PSS). PEDOT is doped with positive ions and PSS with negative ions. It has the following properties that makes it a viable polymer in organic electronics:
- low band gap
- good optical properties
- high conductivity
- low redox potential
- easy processing
- tunable film forming ability
Application
Conductive ink based on the high conductivity grade PEDOT:PSS polymer dispersion. Suitable for deposition and patterning of transparent conductive films using slot die coating and spin coating in OPV application.
PEDOT:PSS can be used as a high conductivity material with a high charge mobility. It can be used for a wide range of energy based applications such as photodetectors, organic photovoltaics (OPV), dye sensitized solar cells (DSSCs), organic light emitting diodes (OLEDs), supercapacitors and other biomedical sensors.
Virtually 100% absorption from 900-2,000 nm. No absorption maximum from 400-800 nm. Conductive polymer blend.
Analysis Note
VLT (excl. substr.) : 80-85%
Work Function: 5.2 -5.4 eV
Coating thickness : 40μm wet
Drying temp. 130°C during 6 min.
Work Function: 5.2 -5.4 eV
Coating thickness : 40μm wet
Drying temp. 130°C during 6 min.
Legal Information
Product of Agfa-Gevaert N.V.
Orgacon is a trademark of Agfa-Gevaert N.V.
Certificates of Analysis (COA)
Search for Certificates of Analysis (COA) by entering the products Lot/Batch Number. Lot and Batch Numbers can be found on a product’s label following the words ‘Lot’ or ‘Batch’.
Already Own This Product?
Find documentation for the products that you have recently purchased in the Document Library.
Our team of scientists has experience in all areas of research including Life Science, Material Science, Chemical Synthesis, Chromatography, Analytical and many others.
Contact Technical Service