Enhanced electrochromic coloration of poly(3-hexylthiophene) films by electrodeposited Au nanoparticles.

Enhanced electrochromic coloration of poly(3-hexylthiophene) films by electrodeposited Au nanoparticles.

Journal of nanoscience and nanotechnology (2013-07-19)

Yoon-Chae Nah

RESUMEN

Au nanoparticles and poly(3-hexylthiophene) (P3HT) composite films were prepared by electrodeposition of Au nanoparticles using pulse-current electrodeposition followed by the spin coating of P3HT and their enhanced electrochromic coloration was investigated. A relatively uniformed Au nanoparticle was obtained by the controlled electrodeposition on indium tin oxide (ITO) substrate and plasmon absorption band of Au nanoparticles were observed. Optical and electrochemical properties of Au/P3HT composite films were compared with the pure P3HT films. The enhanced electrochromic absorption of the composite films was observed due to the surface plasmon resonance of the Au nanoparticles.

MATERIALES

Referencia del producto

Marca

Descripción del producto

Sigma-Aldrich

Gold, foil, thickness 0.1 mm, 99.99% trace metals basis

Sigma-Aldrich

Gold, powder, <45 μm, 99.99% trace metals basis

Sigma-Aldrich

Gold, powder, <10 μm, ≥99.9% trace metals basis

Sigma-Aldrich

Gold, nanopowder, <100 nm particle size, 99.9% trace metals basis

Sigma-Aldrich

Gold, wire, diam. 0.25 mm, ≥99.9% trace metals basis

Sigma-Aldrich

Gold, evaporation slug, diam. × L 0.6 cm × 0.6 cm, 99.99% trace metals basis

Sigma-Aldrich

Gold, foil, thickness 0.025 mm, 99.99% trace metals basis

Sigma-Aldrich

Gold, foil, thickness 0.127 mm, 99.99% trace metals basis

Sigma-Aldrich

Gold, beads, 1-6 mm, 99.999% trace metals basis

Sigma-Aldrich

Gold coated glass slide, layer thickness 100 Å, 99.999% (Au)

Sigma-Aldrich

Gold, wire, diam. 0.5 mm, 99.99% trace metals basis

Sigma-Aldrich

Gold, wire, diam. 1.0 mm, 99.997% trace metals basis

Sigma-Aldrich

Gold coated glass slide, layer thickness 1000 Å, 99.999% (Au)

Sigma-Aldrich

Gold, foil, thickness 0.5 mm, 99.99% trace metals basis

Sigma-Aldrich

Gold, rod, diam. 3.0 mm, 99.99% trace metals basis

Sigma-Aldrich

Gold, powder, <850 μm, ≥99.99% trace metals basis

Sigma-Aldrich

Gold, evaporation slug, diam. × L 0.3 cm × 0.6 cm, 99.99% trace metals basis

Sigma-Aldrich

Gold coated glass cover slip, 99.999% (Au), L × W × thickness 22 mm × 22 mm × 130-170 μm, square, layer thickness 100 Å

Sigma-Aldrich

Gold, wire, diam. 0.1 mm, 99.99% trace metals basis

Sigma-Aldrich

Gold, wire, diam. 1.0 mm, 99.99% trace metals basis

Sigma-Aldrich

Gold, foil, thickness 0.05 mm, 99.99% trace metals basis

Sigma-Aldrich

Gold, wire, diam. 0.5 mm, 99.999% trace metals basis

Sigma-Aldrich

Gold coated glass cover slip, 99.999% (Au), diam. × thickness 15 mm × 130-170 μm, layer thickness 100 Å

Sigma-Aldrich

Gold, wire, diam. 0.25 mm, 99.99% trace metals basis

Sigma-Aldrich

Gold, foil, thickness 0.25 mm, ≥99.9% trace metals basis

Sigma-Aldrich

Gold, wire, diam. 0.127 mm, 99.99% trace metals basis